ELABORATION PAR ICVI ET CARACTERISATION DE COUCHES MINCES B-N-SI POUR APPLICATION COMME INTERPHASES DANS LES MATERIAUX COMPOSITES
CE MEMOIRE PRESENTE L'ETUDE DE DEPOTS EN COUCHES MINCES DANS LE TERNAIRE B-N-SI EN VUE D'AMELIORER LA STABILITE A L'AIR A TEMPERATURE AMBIANTE ET LA RESISTANCE A L'OXYDATION DE MATERIAUX UTILISES COMME INTERPHASES DANS LES COMPOSITES SIC/SIC. LES INTERPHASES B-N-SI SONT REALISEES...
Сохранить в:
| Главный автор: | |
|---|---|
| Другие авторы: | |
| Формат: | Thèse et Mémoire papier |
| Язык: | Français |
| Опубликовано: |
[S.l.] :
[s.n.]
1998.
|
| Предметы: | |
| Примечание: |
1998ORLE2029 |
| Autres localisations: | Voir dans le Sudoc |
| Variante du titre: | ICVI AND CHARACTERIZATION OF B-N-SI THIN FILMS FOR APPLICATION AS INTERPHASES IN COMPOSITE MATERIALS |
| Итог: | CE MEMOIRE PRESENTE L'ETUDE DE DEPOTS EN COUCHES MINCES DANS LE TERNAIRE B-N-SI EN VUE D'AMELIORER LA STABILITE A L'AIR A TEMPERATURE AMBIANTE ET LA RESISTANCE A L'OXYDATION DE MATERIAUX UTILISES COMME INTERPHASES DANS LES COMPOSITES SIC/SIC. LES INTERPHASES B-N-SI SONT REALISEES PAR INFILTRATION CHIMIQUE ISOTHERME (ICVI) A PARTIR DE MELANGES GAZEUX BCI#3-NH#3-CH#3SICI#3-H#2. ON A FAIT VARIER LES PARAMETRES DE DEPOT AFIN D'OBTENIR DES DEPOTS PRESENTANT UNE UNIFORMITE EN EPAISSEUR SUFFISANTE ET DES TENEURS VARIABLES EN SILICIUM. LA COMPOSITION DES DEPOTS B-N-SI A ETE ETUDIEE PAR TECHNIQUES NUCLEAIRES, ALORS QUE LA NATURE DES LIAISONS CHIMIQUES ETAIT DETERMINEE PAR SPECTROSCOPIE DE PHOTOELECTRONS X. LA MICROSTRUCTURE DE CES DEPOTS A ETE ETUDIEE PAR MICROSCOPIE ELECTRONIQUE EN TRANSMISSION. LES TECHNIQUES NUCLEAIRES (RETRODIFFUSION DE RUTHERFORD ET REACTIONS NUCLEAIRES) ONT PERMIS D'ETUDIER LA STABILITE A L'AIR, A TEMPERATURE AMBIANTE, DES COUCHES MINCES B-N-SI. L'ETUDE DE LEUR RESISTANCE A L'OXYDATION A ETE REALISEE PAR ANALYSE THERMOGRAVIMETRIQUE. LES DEPOTS B-N-SI PEUVENT ETRE CLASSES SUIVANT TROIS GRANDES CATEGORIES : LES MATERIAUX DE TYPE A, REALISES POUR DE FAIBLES TENEURS EN CH#3SICL#3 (OU MTS) CONTIENNENT DES TENEURS EN SILICIUM INFERIEURES A 1% ET PRESENTENT UNE MICROSTRUCTURE VOISINE DE CELLE DU BN DEPOSE PAR ICVI. LES MATERIAUX DE TYPE B, REALISES POUR DES TENEURS EN MTS INTERMEDIAIRES, PRESENTENT UNE MICROSTRUCTURE A GRANDES DISTANCES INTERPLANS DONT LE DEGRE D'AMORPHISATION CROIT AVEC LA TENEUR EN SILICIUM. LES DEPOTS B-N-SI DE TYPE C SONT LES MATERIAUX LES PLUS RICHES EN SILICIUM (JUSQU'A 20-30%). ILS SONT AMORPHES ET SONT LES SEULS A PRESENTER UNE STABILITE A L'AIR ET UNE RESISTANCE A L'OXYDATION SATISFAISANTES. DES COMPOSITES SIC/SIC ONT ETE REALISES EN UTILISANT COMME INTERPHASE LES DIFFERENTS TYPES DE MATERIAUX B-N-SI. LES RESULTATS MECANIQUES OBTENUS SUR CES COMPOSITES SONT EN GENERAL INFERIEURS A CEUX OBTENUS SUR LES COMPOSITES A INTERPHASE BN. |
|---|---|
| Примечание: | 1998ORLE2029 |
| Объем: | 337 P. |
| Библиография: | 384 REF. |