ELABORATION ET CARACTERISATION D'OXYNITRURES MIXTES D'ALUMINIUM ET DE LANTHANIDES, NOUVEAUX MATERIAUX DE TYPE MAGNETOPLUMBITE
TOUTE UNE SERIE DE COMPOSES NOUVEAUX A ETE MISE EN EVIDENCE DANS LES SYSTEME LN#2O#3-AL#2O#3-ALN (LN=LANTHANIDE). CES OXYNITRURES, DE STRUCTURE TYPE MAGNETOPLOMBITE ET DE FORMULE LNAL#1#2O#1#8N, PEUVENT ETRE CONSIDERES COMME LA STABILISATION PAR L'AZOTE DES ALUMINATES DE LANTHANIDES BIEN CONNUS...
Kaydedildi:
| Yazar: | |
|---|---|
| Diğer Yazarlar: | |
| Materyal Türü: | Thèse et Mémoire papier |
| Dil: | Français |
| Baskı/Yayın Bilgisi: |
[S.l.] :
[s.n.]
1989.
|
| Konular: | |
| Not: |
1989PA066514 |
| Autres localisations: | Voir dans le Sudoc |
| Variante du titre: | ELABORATION AND CHARACTERIZATION OF LANTHANIDE ALUMINUM OXINITRIDES WITH MAGNETOPLUMBITE-LIKE STRUCTURE |
| Özet: | TOUTE UNE SERIE DE COMPOSES NOUVEAUX A ETE MISE EN EVIDENCE DANS LES SYSTEME LN#2O#3-AL#2O#3-ALN (LN=LANTHANIDE). CES OXYNITRURES, DE STRUCTURE TYPE MAGNETOPLOMBITE ET DE FORMULE LNAL#1#2O#1#8N, PEUVENT ETRE CONSIDERES COMME LA STABILISATION PAR L'AZOTE DES ALUMINATES DE LANTHANIDES BIEN CONNUS LNAL#1#1O#1#8. LA PRESENCE D'AZOTE (N#3#) DANS LA MAILLE CRISTALLINE A ETE DECELEE DIRECTEMENT OU INDIRECTEMENT PAR DIFFERENTES METHODES (DIFFRACTION X, SPECTROSCOPIE XPS, IR, RPE...). AU COURS DU TRAITEMENT THERMIQUE EN ATMOSPHERE OXYDANTE, CET AZOTE N#3# CONDUIT A UN AZOTE NON CHARGE N#0 QUI S'ELIMINE ENSUITE. L'ETUDE DU PROCESSUS D'OXYDATION A ETE SUIVI PAR ATD-ATG COUPLEES AINSI QUE PAR LES TECHNIQUES SPECTROSCOPIQUES PRECEDENTES. UNE INTERPRETATION DES DIFFERENTS PHENOMENES AINSI MIS EN EVIDENCE, EN RELATION AVEC LA NATURE DE L'AZOTE, PRESENT A CHAQUE ETAPE DE L'OXYDATION, A ETE DONNEE. QUELQUES PROPRIETES DE CES OXYNITRURES, PRINCIPALEMENT LEURS PROPRIETES MECANIQUES, ONT ETE ETUDIEES. CES MATERIAUX POURRAIENT ETRE SUSCEPTIBLES D'APPLICATION DANS LE DOMAINE DES CERAMIQUES A HAUTES CARACTERISTIQUES THERMOMECANIQUES COMME LE SONT DEJA LES LIALON ET LES ALON |
|---|---|
| Diğer Bilgileri: | 1989PA066514 |
| Fiziksel Özellikler: | 30 cm. |
| Bibliyografya: | 60 REF |