STRUCTURE DE LA PHASE METASTABLE ZR 1 XAL XO 2 X / 2 ELABOREE PAR VOIE CHIMIQUE : EFFET DE LA SYNTHESE
LA CRISTALLISATION DE POUDRES AMORPHES D'OXYDES MIXTES ELABOREES A PARTIR DE PRECURSEURS LIQUIDES INTERVIENT SOUVENT A DES TEMPERATURES (400\C-900\C) POUR LESQUELLES LA DIFFUSION EST TRES LIMITEE. ELLE PEUT CONDUIRE PAR EXEMPLE A DES PHASES METASTABLES OU A UNE EXTENSION DES DOMAINES DE SOLUTIO...
Tallennettuna:
| Päätekijä: | |
|---|---|
| Muut tekijät: | |
| Aineistotyyppi: | Thèse et Mémoire papier |
| Kieli: | Français |
| Julkaistu: |
[S.l.] :
[s.n.]
1999.
|
| Aiheet: | |
| Huomautus: |
1999ORLE2016 |
| Autres localisations: | Voir dans le Sudoc |
| Yhteenveto: | LA CRISTALLISATION DE POUDRES AMORPHES D'OXYDES MIXTES ELABOREES A PARTIR DE PRECURSEURS LIQUIDES INTERVIENT SOUVENT A DES TEMPERATURES (400\C-900\C) POUR LESQUELLES LA DIFFUSION EST TRES LIMITEE. ELLE PEUT CONDUIRE PAR EXEMPLE A DES PHASES METASTABLES OU A UNE EXTENSION DES DOMAINES DE SOLUTIONS SOLIDES. DANS LE CAS DE LA ZIRCONE, CE MODE D'ELABORATION PERMET L'OBTENTION DE SOLUTIONS SOLIDES ETENDUES A TEMPERATURE AMBIANTE AVEC DES DOPANTS DE TAILLE TRES INFERIEURE A ZR 4 +. L'ETUDE DU SYSTEME ZRO 2-AL 2O 3 A ETE ENTREPRISE AFIN DE MONTRER L'INFLUENCE DE LA SYNTHESE DES PRECURSEURS AMORPHES SUR LA LIMITE DE SOLUBILITE DE AL 2O 3 DANS L'OXYDE DE ZIRCONIUM ET DE MIEUX COMPRENDRE LES MECANISMES DE STABILISATION DE LA ZIRCONE PAR UN CATION DE TAILLE REDUITE COMME AL 3 +. LA SOLUTION SOLIDE METASTABLE ZR 1 XAL XO 2 X / 2 A ETE OBTENUE PAR CRISTALLISATION DE PRECURSEURS AMORPHES SYNTHETISES PAR PRECIPITATION ET ATOMISATION. L'EXTENSION DU DOMAINE DE SOLUTION SOLIDE EST FONCTION DE LA SYNTHESE. LE COMPORTEMENT A LA CRISTALLISATION DE CES PRECURSEURS A PU ETRE CORRELE A L'ENVIRONNEMENT LOCAL DE L'ALUMINIUM. LA DIFFRACTION DES RAYONS X ET LA SPECTROSCOPIE RAMAN ONT MIS EN EVIDENCE UNE SYMETRIE DE TYPE QUADRATIQUE POUR CETTE SOLUTION SOLIDE. DE PLUS, LES SPECTROSCOPIES D'ABSORPTION X (EXAFS DU ZIRCONIUM) ET DE RMN (MAS ET MULTI-QUANTA MAS 2 7AL) ONT ETE MISE EN UVRE AFIN DE DETERMINER LA STRUCTURE LOCALE AUTOUR DES CATIONS ZR 4 + ET AL 3 + ET DE PRECISER LA LOCALISATION DES LACUNES D'OXYGENE. L'ETUDE DU SYSTEME TERNAIRE ZRO 2-Y 2O 3-AL 2O 3 A PERMIS DE MONTRER L'EFFET DE LA PRESENCE D'UN CATION DE GRANDE TAILLE COMME Y 3 + SUR LA REPARTITION DES LACUNES ET LA DISTRIBUTION DES CATIONS AL 3 + DANS LA STRUCTURE. ENFIN, L'ETUDE COMPLEMENTAIRE DES SYSTEMES ZRO 2-FE 2O 3 ET ZRO 2-GA 2O 3 A MONTRE UNE DIFFERENCE DE COMPORTEMENT DU CATION AL 3 + PAR RAPPORT A DES CATIONS DE TAILLE ANALOGUE COMME FE 3 + ET GA 3 +. |
|---|---|
| Huomautukset: | 1999ORLE2016 |
| Ulkoasu: | 145 p. |
| Bibliografia: | 140 ref. |