Residual Stress and Its Effects on Fatigue and Fracture : Proceedings of a Special Symposium held within the 16th European Conference of Fracture - ECF16, Alexandroupolis, Greece, 3-7 July, 2006
Simplified fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineering components under normal and abnormal service loads. In...
Enregistré dans:
| Auteur principal: | |
|---|---|
| Format: | Livre numérique |
| Langue: | Anglais |
| Publié: |
Dordrecht :
Springer Netherlands
2006.
Cham : Springer Nature |
| Accès en ligne: | Accès sur la plateforme de l'éditeur Accès sur la plateforme Istex Accès Université d'Orléans Accès INSA CVL |
| Note: |
Archives Springer e-books (Licence nationale) Archives Springer e-books (Licence nationale) |
| Autres localisations: | Voir dans le Sudoc |
| Edition sous un autre format: | • Residual Stress and Its Effects on Fatigue and Fracture, 9789048173426 • Residual Stress and Its Effects on Fatigue and Fracture, 9789048110766 • Residual stress and its effects on fatigue and fracture, Proceedings of a special symposium held within the 16th European conference of fracture - ECF16, Alexandroupolis, Greece, 3-7 July, 2006, organized by A. G. Youtsos, 2006, Dordrecht, Springer, 1 vol. (X-234 p.), 978-1-4020-5328-3 |
| Résumé: | Simplified fracture mechanics based assessment methods are widely used by the industry to determine the structural integrity significance of postulated cracks, manufacturing flaws, service-induced cracking or suspected degradation of engineering components under normal and abnormal service loads. In many cases, welded joints are the regions most likely to contain original fabrication defects or cracks initiating and growing during service operation. Various procedures provide upper bound residual stress profiles for various classes of welded joints that can be used in fracture assessments, but these often give very conservative results. Recently, the option to use more realistic profiles has been adopted, but only where such profiles are based on finite element residual stress simulations supported by detailed residual stress measurements. Rapid advances in the capability of residual stress measurement techniques, such as the contour and deep hole drilling techniques as well as the neutron and synchrotron X-ray diffraction methods, now readily allow residual stresses and strains to be mapped on defined planes within a structure. The contents of this book have been grouped into three topic areas covering theoretical /numerical and experimental analyses of residual stress and its effects on fatigue and fracture. |
|---|---|
| Description: | Archives Springer e-books (Licence nationale) Archives Springer e-books (Licence nationale) |
| Format: | Nécessite un lecteur de fichier PDF |
| ISBN: | 1402053290 9781402053290 |
| Accès: | Accès en ligne pour les établissements français bénéficiaires des licences nationales Accès soumis à abonnement pour tout autre établissement Conditions particulières de réutilisation pour les bénéficiaires des licences nationales. https://www.licencesnationales.fr/springer-nature-ebooks-contrat-licence-ln-2017 |