ETUDE DE L'INFLUENCE DU PROCEDE D'ELABORATION SUR LA CRISTALLISATION STABLE OU METASTABLE : CAS DU SYSTEME AL#2O#3-Y#2O#3
L'ELABORATION DE MATERIAUX A PARTIR D'UNE PHASE DESORDONNEE SOLIDE (POUDRE AMORPHE) OU LIQUIDE (ETAT FONDU) PEUT CONDUIRE A LA FORMATION DE PHASES METASTABLES. LE SYSTEME AL#2O#3-Y#2O#3 PRESENTE LES DIFFERENTS TYPES DE METASTABILITE RENCONTRES DANS LES MATERIAUX OXYDES. LE PREMIER CHAPITRE...
সংরক্ষণ করুন:
| প্রধান লেখক: | |
|---|---|
| অন্যান্য লেখক: | |
| বিন্যাস: | Thèse et Mémoire papier |
| ভাষা: | Français |
| প্রকাশিত: |
[S.l.] :
[s.n.]
1994.
|
| বিষয়গুলি: | |
| টীকা: |
1994ORLE2025 |
| Autres localisations: | Voir dans le Sudoc |
| Variante du titre: | THE INFLUENCE OF THE METHOD OF PREPARATION ON THE STABLE OR METASTABLE CYRSTALLISATION IN THE AL#2O#3-Y#2O#3 SYSTEM |
| LEADER | 03206nam a22002777a 4500 | ||
|---|---|---|---|
| 001 | 196964 | ||
| 008 | 990313s1994 xxe ||| |||| 00| 0 fre d | ||
| 009 | PPN043951805 | ||
| 041 | 0 | |a fre |b fre | |
| 084 | |a 001.C.01.C.04 | ||
| 084 | |a 540 | ||
| 100 | 1 | |a Le Floch, Sylvie. | |
| 240 | 1 | 0 | |a THE INFLUENCE OF THE METHOD OF PREPARATION ON THE STABLE OR METASTABLE CYRSTALLISATION IN THE AL#2O#3-Y#2O#3 SYSTEM |
| 245 | 1 | 0 | |a ETUDE DE L'INFLUENCE DU PROCEDE D'ELABORATION SUR LA CRISTALLISATION STABLE OU METASTABLE : |b CAS DU SYSTEME AL#2O#3-Y#2O#3 |c SYLVIE LE FLOCH ; SOUS LA DIRECTION DE M. GERVAIS. |
| 260 | |a [S.l.] : |b [s.n.], |c 1994. | ||
| 300 | |a 150 P. | ||
| 500 | |a 1994ORLE2025 | ||
| 502 | |a Thèse de doctorat. Chimie. Orléans. 1994 | ||
| 504 | |a 93 REF. | ||
| 520 | |a L'ELABORATION DE MATERIAUX A PARTIR D'UNE PHASE DESORDONNEE SOLIDE (POUDRE AMORPHE) OU LIQUIDE (ETAT FONDU) PEUT CONDUIRE A LA FORMATION DE PHASES METASTABLES. LE SYSTEME AL#2O#3-Y#2O#3 PRESENTE LES DIFFERENTS TYPES DE METASTABILITE RENCONTRES DANS LES MATERIAUX OXYDES. LE PREMIER CHAPITRE RAPPELLE QUELQUES DONNEES THEORIQUES SUR LES DIAGRAMMES DE PHASES STABLES ET METASTABLES ET DETAILLE LES TECHNIQUES EXPERIMENTALES MISES EN UVRE: ANALYSES THERMIQUES, RMN (#2#7AL, #1#7O, #8#9Y) DU SOLIDE ET DU LIQUIDE, SPECTROMETRIE INFRAROUGE, EXAFS (SEUIL K DE L'YTTRIUM). LE SECOND CHAPITRE DECRIT ET COMPARE LES PHASES ELABOREES PAR DEUX VOIES CHIMIQUES ET TENTE DE MONTRER L'INFLUENCE DE LA SYNTHESE. PLUSIEURS FACTEURS INTERFERENT: ORDRE LOCAL DANS LA PHASE AMORPHE, DECOMPOSITION DE LA MATRICE ORGANIQUE, TEXTURE DES POUDRES ET TAILLE DES GRAINS. CHAQUE VOIE DE SYNTHESE A PERMIS L'OBTENTION D'UNE NOUVELLE PHASE METASTABLE. LE TROISIEME CHAPITRE RAPPORTE LES RESULTATS OBTENUS PAR SOLIDIFICATION EN FONCTION DE LA TEMPERATURE MAXIMALE ATTEINTE PAR LE LIQUIDE. UNE TEMPERATURE SEUIL, T#S#L, A ETE MISE EN EVIDENCE. LE COMPORTEMENT DU LIQUIDE A LA SOLIDIFICATION EST MODIFIE DE FACON IRREVERSIBLE DES QUE SA TEMPERATURE A DEPASSE T#S#L. DEUX CHEMINS DE SOLIDIFICATION METASTABLE PEUVENT ALORS ETRE OBSERVES SUIVANT LA VITESSE DE REFROIDISSEMENT. LA METASTABILITE SEMBLE LIEE A LA DIFFICULTE DE NUCLEATION DE Y#3AL#5O#1#2. LE DERNIER CHAPITRE EST CONSACRE A L'ETUDE STRUCTURALE D'UNE SOLUTION SOLIDE METASTABLE DE TYPE GRENAT QUI SE FORME PAR CRISTALLISATION DES POUDRES AMORPHES ET SOLIDIFICATION DU LIQUIDE. LA PRESENCE D'ENTITES TETRAEDRIQUES ALO#4 DANS LA POUDRE AMORPHE COMME DANS LE LIQUIDE SEMBLE INFLUENCER LA NATURE DES PHASES QUI CRISTALLISENT | ||
| 650 | |a Thèses et écrits académiques | ||
| 700 | 1 | |a Gobillon-Gervais, Monique. |4 ths | |
| 710 | 2 | |a Université d'Orléans. |4 dgg | |
| 787 | 0 | 8 | |i Reproduced as: |0 24623346X |t ETUDE DE L'INFLUENCE DU PROCEDE D'ELABORATION SUR LA CRISTALLISATION STABLE OU METASTABLE |o CAS DU SYSTEME AL#2O#3-Y#2O#3 |f SYLVIE LE FLOCH |c Grenoble |n Atelier national de reproduction des thèses |d 1994 |p Microfiches |s [Grenoble thèses] |
| 997 | |0 196964 |1 Thèse et Mémoire papier |a Ressource papier |c 0/Orléans/ |c 1/Orléans/BU Sciences, Technologies, STAPS/ |z Orléans, BU Sciences, Technologies, STAPS, TS 19-1994-25 |z Orléans, BU Sciences, Technologies, STAPS, TS 19-1994-25b | ||
| 999 | |5 452342104:051163489 |a ORLEANS | ||